Chemical-microorganism combined with PTMS Electromagnetic Separator removed NO.4 ferric trioxide, thiourea dioxide as reducing agent, the slurry concentration was 20%, the amount of thiourea dioxide was 4%, the initial pH was 10, the reaction time was 60min, and the reaction temperature was 65℃. The content of iron oxide decreased from 0.69% to 0.48%, the natural whiteness increased from 62.5% to 80.1%, and the 1280℃ burning whiteness increased from 82.7% to 88.7%.

PTMS magnetic separation

 
Chemical bleaching conditions, and further PTMS Electromagnetic Separator for iron removal. On day 3, the ferriO content decreased from 0.48% to 0.43%, the natural whiteness increased from 62.5% to 81.2%, and the 1280℃ C firing whiteness increased from 82.7% to 89.0%. NO.1, NO.2 and NO.3.

what is magnetic separation in Kaolin？

 
The results showed that on the fourth day, the content of NO.1 decreased from 0.66% to 0.38%, the natural whiteness increased from 66.3% to 75.7%, and the 1280℃ increased from 83.6% to 89.0%. On day 8, the content of NO.2 kaolin decreased from 0.94% to 0.38%, natural whiteness increased from 51.5% to 82.2%, and 1280℃ calcined whiteness increased from 78.5% to 92.3%. PTMS Electromagnetic Separator Iron removal was significant.
Contact: DELLA
Mob: +86-13929907491
sales@powtechina.com